Experimental investigation of pinned joints in ncf glass-fibre reinforced composite plates

Abstract

In this study, mechanical behaviour of quasi-unidirectional (quasi-UD) non-crimp fabric (NCF) reinforced composite plates with pinned joints was investigated experimentally. Composite laminates with three different cross-ply and three different quasi-isotropic layups were manufactured with vacuum assisted resin transfer moulding (VARTM) method. The pin-bearing tests of the specimens were completed according to ASTM D5961 standard. Test results were compared with a different material system and joint configuration. Finally, the cross-sections of damaged areas were inspected with optical microscopy.Bu çalışmada, pim bağlantısına sahip yarı-tek yönlü cam kıvrımsız elyaf (KE) takviyeli kompozit plakaların mekanik davranışları deneysel olarak incelenmiştir. Üç farklı çapraz-katlı ve üç farklı yarı-izotropik elyaf sıralamasına sahip kompozit plakalar vakum destekli reçine transfer yöntemi (VARTM) ile üretilmiştir. Deney numunelerinin pim bağlantısı testleri ASTM D-5961 test standardına göre yapılmıştır. Test sonuçları farklı malzeme ve bağlantı sistemleriyle karşılaştırılmıştır. Son olarak, delik çevresinde hasar oluşan bölgelerin kesitleri optik mikroskopta incelenmiştir.