Conductivity measurements with multilayered langmuir blodgett films produced by 4-methylbenzenethiol encapsulated gold nanoparticles and two kinds of peo derivative containing li+ ions

Abstract

Langmuir – Blodgett (LB) thin film technique has been used to fabricate thin films of thiol-coated gold nanoparticles and lithium-doped poly(ethylene oxide) (PEO) derivative matrix. These thin films have been fabricated on interdigitated gold electrodes. Electrical measurements have been made using these thin films containing 4-32 layers. I-t measurements for all films showed that the current passing through is stable with time. The I-V measurements showed that the current passing through the Langmuir-Blodgett films is in the µA and nA (for 0-5V bias) region for nanoparticles and PEO respectively and that the presence of ions in the films modifies the conductivity.Thiol ile kaplanmış altın nanoparçacıklar ve lityum dop edilmiş polyetilen oksit (PEO) matrisi Langmuir – Blodgett (LB) ince film üretiminde kullanılmıştır. Bu ince filmler interdijite altın elektrotlar üzerine oluşturulmuştur. 4-32 tabaka içeren bu filmler kullanılarak elektriksel ölçümler yapılmıştır. Tüm filmler için yapılan I-t ölçümleri akımın zamanla sabit olduğunu göstermiştir. I-V ölçümleri LB ince film üzerinden geçen akımın nanoparçacıklar ve polyetilen oksit (PEO) için sırasıyla µA ve nA (0-5V aralığı için) mertebesinde olduğunu ve film içinde iyon varlığının iletimi değiştirdiğini göstermiştir.