Investigation of wear properties of quartz filled polyester composites

Abstract

Weight loss and wear resistance were examined in the wear of polyester composites with quartz filling. In the load system applied to the sample in wear machine, an abrasive attached to a steel plate that applies axial pressure on the surface of sample carries out a linear reciprocating motion and rubs on the composite surface. Working loads are 10, 20 and 30 N. Application times are 10, 20, 30, 40, 50 and 60 minutes. At the end of test, it was seen that weight losses increased with the increasing load and time. Composite type B had a low weight loss and great wear resistance. For composite B, max weight loss and abrasion resistance values were 0,1949 g and 4,4334 Nm/m(3), respectively.Kuvars dolgu malzemeli polyester kompozitlerin aşınma olayında ağırlık kaybı ve aşınma direnci incelenmiştir. Aşınma makinesinde numuneye uygulanan yük sistemi, numunenin yüzeyine yatay olarak baskı yapan bir çelik plakada bağlı bir aşındırıcının doğrusal gidip gelme hareketi yaparak, kompozit yüzeyine sürtünmesiyle çalışır. Çalışma yükleri 10, 20 ve 30 N’dur. Uygulanan süreler 10, 20, 30, 40, 50 ve 60 dakika’dır. Deneyler sonucunda artan yük ve süre ile ağırlık kayıplarının arttığı belirlenmiştir. Kompozit tiplerinden B, düşük ağırlık kaybı ve büyük aşınma direncine sahip olmuştur. B kompozit tipi için ağırlık kaybı ve aşınma direnci en büyük değerleri sırasıyla 0,1949 g ve 4,4334 Nm/m3 olmuştur.